Polyglide TU-P is a 30% glass reinforced, heat stabilized resin containing Teflon / PTFE Micropowder. It is designed for highly reduced friction in applications requiring low wear and/or low friction against itself, steel, or other plastics.
Self-lubricating
Corrosion resistance
Best material to use with soft shaft materials
Low moisture absorption
Vibration dampening
Low coefficients of friction
Maintenance free
Low weight
High wear resistance
Very good price performance ratio
| Property | Test Method | Units | Value DAM |
|---|---|---|---|
| Mechanical | |||
| Stress at Break | ISO 527 | MPa (kpsi) | 185 (26.8) |
| Strain at Break | ISO 527 | % | 2.8 |
| Tensile Modulus | ISO 527 | MPa (kpsi) | 10300 (1500) |
| Flexural Modulus | ISO 178 | MPa (kpsi) | 9200 (1330) |
| Flexural Strength | ISO 178 | MPa (kpsi) | 270 (39.2) |
| Notched Charpy Impact Strength | ISO 179/1eA | kJ/m2 | 13 |
| Unnotched Charpy Impact Strength | ISO 179/1eU | kJ/m2 | 80 |
| Thermal | |||
| Deflection Temperature | ISO 75-1/-2 | °C (°F) | |
| 1.80MPa | 250 (482) | ||
| Melting Temperature | ISO 11357-1/-3 | °C (°F) | |
| 10°C/min | 263 (505) | ||
| Other | |||
| Density | ISO 1183 | kg/m3(g/cm3) | 1500 (1.50) |